LOW HYDROGEN IRON POWDER ELECTRODE FOR WELDING STEELS WITH A MINIMUM UTS OF 700 N/mm2
RD-100D2
CLASSIFICATION
AWS A5.5 E10018-D2 | EN ISO 18275-A E 62 5 MnMo B
PRODUCT DESCRIPTION
The design emphasis of the chemically basic flux is engineered to ensure the optimum weld metal properties demanded by the specification are fully met. The basic flux containing the appropriate alloying elements with a controlled balanced addition of iron power, is extruded onto a high purity ferritic core wire with a blend of silicates that ensures both coating strength and a coatingresistant to subsequent moisture absorption
WELDING FEATURES OF THE ELECTRODE
The chemical nature of the flux together with a significant proportion of iron powder ensures maximum deposition efficiency without detracting from its ability to be used in all positions except vertical down. Overall the arc is very stable, slag detachability is good and metal recovery is some 115% with respect to the core wire.
APPLICATIONS AND MATERIALS TO BE WELDED
Suitable for welding steels with a minimum UTS of 700 N/mm2 meeting the properties both as welded or after PWHT. Typical materials include ASTM A514 used for pressure vessels, bridges and offshore constructional work. The addition of Mo increases weld metal strength at elevated temperature and maintains UTS after PWHT and provides increased resistance to corrosion.
WELDING AMPERAGE AC and DC
OTHER DATA
Electrodes that have become damp should be re-dried at 150oC for 1 hour