FOR WELDING LOW CARBON AUSTENITIC STAINLES STEELS CONTAINING A NOMINAL 19Cr and 10Ni
NSN-308L
CLASSIFICATION
AWS A5.4 E308L-16 | EN ISO 3581-A E 19 9 L R | JIS Z 3221 D308L-16
PRODUCT DESCRIPTION
A metallurgically advanced rutile based flux formulated with balanced additions of chemically basic, amphoteric and acid minerals, together with small alloy additions to compensate for arc losses. The flux is concentrically extruded onto a fully alloyed core wire and bound by a blend of silicates that assures both coating strength and resistance to subsequent moisture absorption
WELDING FEATURES OF THE ELECTRODE
This unique flux formulation ensures excellent arc stability, ease of initial arc strike and re-strike minimal spatter on AC and virtually none on DC+. The resultant weld seams are smooth, evenly rippled and free from undercut while slag detachability is excellent. Metal recovery is some 103% with respect to core wire weight.
APPLICATIONS AND MATERIALS TO BE WELDED
Applications for the electrode are to be found in the Chemical, Petro-Chemical and Cryogenic Processing and Storage Industries as well as the Food, Brewery and Pharmaceutical Industries using the following materials: ASTM 304L 304 304LN CF3 CF8 UNS S30403 S30400 S30453 Plus ASTM 301, 302 and 303. For all of the above, NSN-308L ensures matching resistance to corrosion
WELDING AMPERAGE AC and DC
OTHER DATA
Electrodes that have become damp should be re-dried at 150oC for 1 hour
APPROVED BY
LR Grade 304L